Yes, I have been thinking about this but pieces 4 mm + 4 mm both were guardian cut from the same sheet of glass and still, they are not completly flat (but definitly better than 4 mm gluardian + 6 mm pilkington).
Mundek
Search found 7 matches
- Mon Apr 01, 2019 10:47 am
- Forum: Techniques and Tools
- Topic: float glass fusing problem - bends
- Replies: 11
- Views: 13098
- Mon Apr 01, 2019 1:26 am
- Forum: Techniques and Tools
- Topic: float glass fusing problem - bends
- Replies: 11
- Views: 13098
Re: float glass fusing problem - bends
Yes, we fuse 2 pieces:
900 x 300 x 4 + 900 x 300 x 6 (6 mm thick piece lays on 4 mm thick piece). Total is 10 mm. Both are float, 4mm - guardian, 6mm - pilkington.
Mundek
900 x 300 x 4 + 900 x 300 x 6 (6 mm thick piece lays on 4 mm thick piece). Total is 10 mm. Both are float, 4mm - guardian, 6mm - pilkington.
Mundek
- Sun Mar 31, 2019 11:13 am
- Forum: Techniques and Tools
- Topic: float glass fusing problem - bends
- Replies: 11
- Views: 13098
Re: float glass fusing problem - bends
Hello Brad,
After tests as per your recommendation, result is still the same - only 900x300x4 + 900x300x4 is better (almost flat). All pieces where we melt 6 mm thick glass plus 4 mm are bent.
Do you have any other idea whats wrong?
Mundek
After tests as per your recommendation, result is still the same - only 900x300x4 + 900x300x4 is better (almost flat). All pieces where we melt 6 mm thick glass plus 4 mm are bent.
Do you have any other idea whats wrong?
Mundek
- Fri Mar 22, 2019 2:36 pm
- Forum: Techniques and Tools
- Topic: float glass fusing problem - bends
- Replies: 11
- Views: 13098
Re: float glass fusing problem - bends
Thank you very much.
Will conduct tests and till the end of coming week let you know about the progress.
Regards,
Mundek
Will conduct tests and till the end of coming week let you know about the progress.
Regards,
Mundek
- Fri Mar 22, 2019 12:00 pm
- Forum: Techniques and Tools
- Topic: float glass fusing problem - bends
- Replies: 11
- Views: 13098
Re: float glass fusing problem - bends
Thank you very much for a suggestion. Below is new schedule, could you check and let me know did I understood right your suggestions ? 0 C – 482 C in 120 min stay 15 min 482 C – 593 C in 20 min stay 0 min 593 C – 676 C in 90 min stay 30 min 676 C – 801 C AFAP stay 10 min 801 C – 620 C AFAP stay 30 t...
- Fri Mar 22, 2019 10:53 am
- Forum: Techniques and Tools
- Topic: float glass fusing problem - bends
- Replies: 11
- Views: 13098
Re: float glass fusing problem - bends
Hello, Yes, fusing was done on flat shelf (on ceramic paper). And yes, saying 'bends' I meant, that bows upward slightly (like you can see on photo attached). Below you can see firing schedule: 0 C – 482 C in 120 min stay 15 min 482 C – 593 C in 20 min stay 0 min 593 C – 676 C in 90 min stay 30 min ...
- Thu Mar 21, 2019 12:14 pm
- Forum: Techniques and Tools
- Topic: float glass fusing problem - bends
- Replies: 11
- Views: 13098
float glass fusing problem - bends
Dear ALL, I am new here and also, quite new in fusing. Probably, the topic is somewhere here but it is not so easy to me with my english to find it. I am trying to fuse 2 pieces of float glass (900x300x4 + 900x300x6). Firing shedule I have found here on the forum as a standard for a float. The probl...