by Brad Walker
Fri May 22, 2020 8:10 am
Forum: Techniques and Tools
Topic: drop ring fell off center
Replies: 2
Views: 52

Re: drop ring fell off center

Looks like it was closer to the elements on one side than the other. Is that possible?
by Brad Walker
Sat Apr 25, 2020 11:06 am
Forum: Techniques and Tools
Topic: can't figure out what I. did different
Replies: 3
Views: 201

Re: can't figure out what I. did different

Generally, blue bubbles come from a copper compound. They'll give you the beautiful bright blue bubbles in your piece. If you put too much copper (usually copper oxide) it will have black ugly areas like your other piece. Firing too high can also cause this problem. My guess is that the mica you're ...
by Brad Walker
Sat Apr 25, 2020 9:01 am
Forum: Techniques and Tools
Topic: can't figure out what I. did different
Replies: 3
Views: 201

Re: can't figure out what I. did different

You sure it's mica powder you added? Looks like copper or a copper oxide.
by Brad Walker
Tue Apr 21, 2020 9:38 pm
Forum: Techniques and Tools
Topic: Does a new kiln controller come already programmed?
Replies: 5
Views: 211

Re: Does a new kiln controller come already programmed?

New controllers do have a program (or programs) in them. It's usually not a full fledged firing schedule, but a few steps that are used to test the controller out.
by Brad Walker
Fri Apr 10, 2020 9:52 pm
Forum: Techniques and Tools
Topic: strange result
Replies: 2
Views: 162

Re: strange result

How high did you fire? You'd have to fire pretty far above normal fusing temperatures to get the glass to flow off the kiln shelf.
by Brad Walker
Wed Apr 08, 2020 8:01 am
Forum: Techniques and Tools
Topic: keeping Texture on glass
Replies: 2
Views: 169

Re: keeping Texture on glass

If you tack fuse at a low enough temperature you'll keep most of the texture. 1350F/730C is high enough to stick glass together and retain most of the texture. The higher above that you go, the more texture you will lose.
by Brad Walker
Sun Apr 05, 2020 9:24 pm
Forum: Techniques and Tools
Topic: transparent glass turns opaque
Replies: 1
Views: 355

Re: transparent glass turns opaque

Very common, especial with reds. The higher the temperature, the more likely.
by Brad Walker
Sat Apr 04, 2020 2:04 pm
Forum: Techniques and Tools
Topic: kiln wash residue
Replies: 9
Views: 325

Re: kiln wash residue

Michael, According to the MSDS, Bullseye thinfire paper is manufactured in Japan by LINTEC Corporation under the name "Paper Ceraform M. " I don't know how difficult it is for you to get product from Japan, but if you want to try, LINTEC's contact information is on this MSDS: https://www.w...
by Brad Walker
Wed Apr 01, 2020 2:47 pm
Forum: Techniques and Tools
Topic: Screen melt bubbles
Replies: 4
Views: 206

Re: Screen melt bubbles

JestersBaubles wrote:Looks to me like you need more glass.


I was thinking the same thing.
by Brad Walker
Fri Mar 27, 2020 1:04 pm
Forum: Techniques and Tools
Topic: How to mount...
Replies: 7
Views: 328

Re: How to mount...

Photo of piece.

IMG_0302.jpeg
by Brad Walker
Thu Mar 26, 2020 7:54 am
Forum: Techniques and Tools
Topic: first attempt with new kiln
Replies: 4
Views: 201

Re: first attempt with new kiln

To help you, we'll need to know what firing schedule you used, what glass as well.

What happened when you tried to upload the picture? What format was it?
by Brad Walker
Mon Mar 16, 2020 8:13 am
Forum: Techniques and Tools
Topic: bottom heat kiln.
Replies: 1
Views: 135

Re: bottom heat kiln.

What does the manufacturer recommend?
by Brad Walker
Fri Mar 13, 2020 8:19 am
Forum: Techniques and Tools
Topic: calculating the amount of glass for a mold
Replies: 4
Views: 407

Re: calculating the amount of glass for a mold

What you want to test is what the glass will look like. Small frit vs large frit, for example, will look very different. And different colors as well. Basically, before you spend a lot of money on glass, spend a little money with a smaller mold to make sure the color and transparency will be what yo...
by Brad Walker
Thu Mar 12, 2020 9:41 pm
Forum: Techniques and Tools
Topic: calculating the amount of glass for a mold
Replies: 4
Views: 407

Re: calculating the amount of glass for a mold

Get a container. Put water in it. Mark the level of the water. Pour some water into the mold. Mark the new, lower level of the water. Now fill the container with glass until the water raises to the original level (the first mark). That's how much glass you need. The smaller the pieces of glass you u...
by Brad Walker
Sat Feb 29, 2020 5:23 pm
Forum: Techniques and Tools
Topic: painting crisp, even thickness lines
Replies: 11
Views: 1096

Re: painting crisp, even thickness lines

There's not a huge difference in the way the Colorline paints work than the Sunshine.

To get an absolutely straight line, use a resist and paint through that, rather than by hand.
by Brad Walker
Sat Feb 29, 2020 9:12 am
Forum: Techniques and Tools
Topic: painting crisp, even thickness lines
Replies: 11
Views: 1096

Re: painting crisp, even thickness lines

We use Sunshine Enamels. Mixed properly, they work like oil paints or acrylics.

Caveat: we also sell them: https://www.warmglass.com/enamels
by Brad Walker
Fri Feb 07, 2020 9:39 am
Forum: Techniques and Tools
Topic: New Studio - New Kiln
Replies: 9
Views: 684

Re: New Studio - New Kiln

I owned a Nabertherm GF240 fiber kiln for nearly 10 years. It performed flawlessly, required less electricity than a smaller brick kiln, and was my go-to kiln for larger projects. Nabertherm is German; the kiln has fiber sides and top, with a brick floor. The fiber is rigid, not blanket. I eventuall...
by Brad Walker
Fri Jan 31, 2020 8:28 am
Forum: Techniques and Tools
Topic: bell kiln repair
Replies: 2
Views: 334

Re: bell kiln repair

For fiber, top only should work.

For brick, both.
by Brad Walker
Sat Jan 25, 2020 9:14 am
Forum: Techniques and Tools
Topic: source for mica flakes
Replies: 14
Views: 9389

Re: source for mica flakes

Michael Stevens wrote:does anyone know if colored micah powders used in. make up can be used in fusing?


Most likely the color will change or fade, but it's worth a try.
by Brad Walker
Mon Jan 13, 2020 8:59 am
Forum: Techniques and Tools
Topic: copper inclusion
Replies: 3
Views: 423

Re: copper inclusion

Michael Stevens wrote:I'm. sorry I meant .2mm


.2mm should be thin enough. Try a small piece as a test.