Take the glass coe 96 fires cooler than the coe 90 just don't mix up the glasses and mix the coe. When they come out of my kiln they all look Gooood. I fire with both and have them in seperate places in the shop.

after 12 years of stained glass the kiln has gotten me hooked on glass again. I used the pre programed programs with the skutt for a couple of weeks and then figured out how to set the kiln at different settings it is great fun each morning to see what comes out. If you changes the temp. besure to k...

I want to apply new wash to stainless steel. But the old won't wash off. it is streakie, not covered well in places and to much in other places. Should i steel wool it off and heat?

Thank you, as soon as I get the supports to hold the pot i will do this.

I am getting ready to try the melt pot thing. Let us know how it turn out.

I want to try the melt pot,

Do i need kiln wash on the melt pot (aka flower pot)? all these scarpes it is nice to use them up.

Thank You, better to ask and better to not take the chance

Thanks
Betty

Just got Uroboros glass frit Mosaic size, and it has a white powder or dust all over the glass pieces. Do I need to remove the dust from the pieces?

The glass i fired last night I cleaned with rubbing alocolce and it looked good this morning.

Betty

I have slumped with youg. glass in a single sheet into a bulleye mold it has come out good the colors have changed and muddied a bit but for a candle holder it is ok.

The small, 4" & 6', molds have not slumped I reset the temp. to 1275 degrees. Hold time is 10 minutes

Just how hot can the mold go before they crack? The glass is only a single layer of fusing glass.

Warner-crivellaro in allentown Pa is fast

http://WWW.Warner-Criv.com.

Do a search under 96-*

there are all kinds of things. the warm glass is only on the internet but they are putting out a new catologe soon.

I would love to change the temp. but the direction are confussing to me. Going away for a week and will call Skutt when i get home.

Rate Soak Hold 400f/hour 600f 5 min 600f/hour by process by process 9999f/hour 960f 40 min 175f/hour 800f 10 min like i said it still makes no sence to me but it willl

It is a new kiln, skutt Hot start, and I am using the preprogramed settings. The insturation are confusing for me.

The firing was medium speed and slump with a soak of 1225 for 15 minutes

Just what all this means i am still learning.

What i am using in the stained art glass. I just want to slump it in some small molds.

I put one piece of glass, not the heat glass just regural glass, in the kiln and it didn't slump in the mold. Won't regural glass slump or does it need to be hotter to slump. there are just so many beautiful glass it seems a shame not to try a few.

It is a pours pottery mold in the shape of a drinking glass. 5.5" tall and in the freezer at the moment. idea from the place i by the molds.

I was thinking about trying to make another mold using this mold as a shape, guess i need to find out how to make molds.

Betty

First slump and the glass is stuck to the mold. I kilned washed it and let it dry 2 days and the glass is stuck.

I have put it in water to soak is there anything else i can do?

Betty