Thank you BERT

So for Temperd I dont have To break at all , or is that just for Tinted ?

That would be Kool , So tinted IN the same as Float ?

I thought I you didnt break It it Would Explode in the Kiln ?

Thanks for answering all my Noob Questions!!!

Bert Weis Said-Tinted tempered glass can be fired as long as you can heat the whole piece at once. After you have reached 1100ºF it is no longer tempered and will behave just like any annealed glass.

I ask does that mean I dont have to break it first if i fire it to 1100

Anyone No any Type of Glass that glows Under a Blacklight other than
"Vasealine Glass" or Uranium glass from the 1890's ?

http://www.glass.co.nz/ (link to Uranium glass site)

Any info on its possible or impossible existence as purchasable item would be amazing !

Friz

Bert Q = So you mean for tinted temperd I dont have to break it first ? I thought that the temperd would explode in the kiln If I didnt snap an edge first. Interesting, that would be kool. Im playin with Devit rite now and am Likeing that effects it has on temperd, particualarily Clear Temperd. Q = ...

Anyone Ever Play with Tinted Tempered Glass before and Wierd results ?
tanks

Im in the Experimenting stager ight now but has Anyonw tried using Kiln Wash as a mold Before ? IM talking about using 2 inch kiln washed post and fillling the midle with kiln wash then evening it out to be flat with the 2 inch posts. Then you have a square "2 inch High Of kiln wash, Use a piec...

Yeah Id like To know Too , I have a Paragon GL-44 ADST

Side And Top elements. !
thanks

ARE THE TWO oTHER Larger peices clear irredecent, Through my experience, kiln wash doesnt stick as much on that type ogf glass.



hope i answerd youR Q for ya

Yes I have read the tutorial here it was very helpful, I also Have the Warm Glass book , I cant say enough good things about this book, great Job. Im sure you have helped alot of people just like myself get into this Artistic Hobby, As for the Kiln Wash TechNick, VERY KOOL It Really Deserves another...

One more question out there, Do you think I can Stack 6 20'' shelves in Kiln, and Fire it up with that much of a Difference in the ytemp from top to Bottom?, Should I stagger the Shelves for better air flow ?

Thanks Alot for any Answers,

I was Fusing All Kinds Of stuff , Tinted tempered, Float, Spectrum

Soo You think I should Flash kool To A higher temp than 1100 ?

I tried To Mold Using Kiln Wash But I left too much space Between The wash and the Float Layers.

Very impressiVe

After you CooL your kiln to Annealing Temp (1100 F)does it matter how long it takes after that to get to Room Temp ?. Is Too Slow Bad,
I have a Large kiln And My Paragon Controller Read FTC,
Meaning Failure Too CooL is this Bad ?

Kinda Looks Like the eye of Ra, The Egiptian Sun God

Remember Star Gate the movie with Kurt Russel, the bad guy Is RA