Hello,
Last month I plays with glass strips.
Here is one of the works. I'd love to hear your comments.
Spectrum glass, 40X20x1.5 cm
Thanks
Osnat
Search found 49 matches
- Sun Nov 11, 2012 11:07 am
- Forum: Photos and Stuff
- Topic: strips work
- Replies: 5
- Views: 7630
- Thu Sep 20, 2012 4:06 pm
- Forum: Techniques and Tools
- Topic: Laminated panel
- Replies: 2
- Views: 3035
Re: Laminated panel
Thanks
Osnat
Osnat
- Thu Sep 20, 2012 5:59 am
- Forum: Techniques and Tools
- Topic: Laminated panel
- Replies: 2
- Views: 3035
Laminated panel
Hi everyone
what is the process of Laminated panel.
Does it a kind of clear decal which is put on the back of the glass ?
Is it enough to make the fusing process , in a big unit, to safe to use in a architecture
Thanks
Osnat
what is the process of Laminated panel.
Does it a kind of clear decal which is put on the back of the glass ?
Is it enough to make the fusing process , in a big unit, to safe to use in a architecture
Thanks
Osnat
- Wed Sep 12, 2012 12:42 pm
- Forum: Techniques and Tools
- Topic: Cutting glass 45 angle
- Replies: 5
- Views: 6292
Re: Cutting glass 45 angle
Thanks evryone.
Osnat
Happy new year
Osnat
Happy new year
- Wed Sep 05, 2012 8:13 am
- Forum: Techniques and Tools
- Topic: Cutting glass 45 angle
- Replies: 5
- Views: 6292
Cutting glass 45 angle
Hello,
What is the way to cut the 3 mm side of the glass in 45 angle.
I hope my q.is clear. I doing a glass strip work,and a design includ kind of triangle.
Thank
Osnat
What is the way to cut the 3 mm side of the glass in 45 angle.
I hope my q.is clear. I doing a glass strip work,and a design includ kind of triangle.
Thank
Osnat
- Sat Aug 04, 2012 8:13 am
- Forum: Techniques and Tools
- Topic: Schedule advice
- Replies: 4
- Views: 5557
Re: Schedule advice
Hello evry one,
I gave glass good conditions, so why do I got 2 pop bubbles.
55 150 15
140 570 10
90 780 15
af 510 120
55 287 10
off room tep.
Thank
Osnat
I gave glass good conditions, so why do I got 2 pop bubbles.
55 150 15
140 570 10
90 780 15
af 510 120
55 287 10
off room tep.
Thank
Osnat
- Fri Jul 27, 2012 12:48 pm
- Forum: Techniques and Tools
- Topic: Schedule advice
- Replies: 4
- Views: 5557
Schedule advice
Hello evryone, I would love to hear your advice about firing Schedule. In must places i re The main factor that effects the anniling process is the thickness of glass.and There are basic schedule at Spectrum web. But what is the effect of the size of the work ? It is clear to me, largerer work need ...
- Tue Jun 19, 2012 7:11 am
- Forum: Techniques and Tools
- Topic: About Devit
- Replies: 11
- Views: 13214
Re: About Devit
Thank you.
Just one more clarification .If the work is after first fire (full fuse)
and got devit, can I apply Borax and slump.
Would it help to remove the Devit?
Thanks
Osnat
Just one more clarification .If the work is after first fire (full fuse)
and got devit, can I apply Borax and slump.
Would it help to remove the Devit?
Thanks
Osnat
- Sun Jun 17, 2012 3:01 pm
- Forum: Techniques and Tools
- Topic: About Devit
- Replies: 11
- Views: 13214
About Devit
Hello everyone, Is there a difference between Glass A and Borax? Glaze A , Powder that mixed with water. It prevent the devit . It does not remove the extent devit. And the fire must be more than 720 c (1328 f) What about Borax, prevent, remove the devit? Min fire? I have read in web (i dont remembe...