Faulty glass? or faulty user? - WarmGlass.com

Faulty glass? or faulty user?

This is the main board for discussing general techniques, tools, and processes for fusing, slumping, and related kiln-forming activities.

Moderators: Tony Smith, Brad Walker

Post Reply
Barbara Muth
Posts: 382
Joined: Sun Mar 09, 2003 8:10 pm
Location: Washington DC Metropolitan Area
Contact:

Re: Faulty glass? or faulty user?

Postby Barbara Muth » Sun Feb 17, 2008 8:37 pm

frizzygirl wrote:Hiya

Thanks Tony, sorry trying to be quick before my laptop battery dies.

Its 222C to 677C with a 30 min hold.
Then 333C to 777C with a 6min hold.

Regards
Tracey


that would be 400 dph to 1250F, hold 30
and then 600 dph to 1430 F, hold 6

So a couple of thoughts... If your base was one layer thick you were going to have problems with volume control at that high a temp. If you wanted to just tack the pieces together you could have done so at a lower temp, say around 1300 F or 700 C. You are ramping up way too fast which is why the piece thermal shocked. And that fast ramp will trap air in a piece as well. You need a bubble squeeze.

Instead try:
200 dph F to 1000F (111 dph C to 538C)
50 dph F to 1250F (28 dph C to 678C)
300 dph F to 1350, hold 15 (167 dph C to 732C)
and then anneal as recommended by your glass manufacturer.
Barbara
Check out the glass manufacturer's recommended firing schedules...
LATEST GLASS

Post Reply

Return to “Techniques and Tools”

Who is online

Users browsing this forum: No registered users and 42 guests

Warm Glass

2575 Old Glory Road, Suite 700
Suite 700
Clemmons, NC 27012
Phone: (336) 712 8003
Email: wg@warmglass.com