'Damming ' with iridescent glass

Post by Havi »

Good morning everybody,
If I dam a piece with iridescent glass - will it save me from cold working the edges of the piece?

I want to do a relatively big piece. I do not want to cold work the edges, therefore was thinking about this kind off solution.

I'd welcome other solutions too, if there are any.



Many thanks in advance,

Havi
Haviva Z
- - - - with a smile :)

"Speed comes from the Devil" - (an Arabic proverb)
Image
http://www.havivaz.com
Barb R
Posts: 58
Joined: Tue Jul 26, 2005 3:02 pm
Location: Ft. Collins, CO

Re: 'Damming ' with iridescent glass

Post by Barb R »

Havi,

Irid will stick to the unfinished sides of your glass - so I don't think it's a good material to use to for a dam. I think you have to have irid to irid before it will not adhere.

Barb
Charlotte Kay
Posts: 15
Joined: Sat Dec 12, 2009 10:43 pm
Location: Northern California

Re: 'Damming ' with iridescent glass

Post by Charlotte Kay »

Hi Havi,

Take a look at Bullseye tip sheet 3 "Working Deep" which uses irid for the sides:

https://www.bullseyeglass.com/methods-i ... -deep.html

Experiment with a small pieces, say 4" or 5" square and 1" deep, and see if the results are what you desire.

This is a trial piece using three layers with powered leaves, using 22 layer of BE Crystal Clear plus irid for the sides, as in the tip sheet. I first fired two layers at a time then stacked them all with the sides and used dams.


Charlotte
Attachments
LeavesinDeep.jpeg
LeavesinDeep.jpeg (37.59 KiB) Viewed 7230 times
Havi
Posts: 619
Joined: Wed Jul 02, 2003 6:01 am
Location: Israel
Contact:

Re: 'Damming ' with iridescent glass

Post by Havi »

Thanks Charlotte,

I knew I read it somewhere.

I want to make a relatively big rectangle - but I do not want to deal with coldworking, this the reason why I asked about in the first place.
I'd rather not do the piece at all then having to coldwork its edges, strange as it may sound.


Thanx a lot,

Havi
Haviva Z
- - - - with a smile :)

"Speed comes from the Devil" - (an Arabic proverb)
Image
http://www.havivaz.com
Charlotte Kay
Posts: 15
Joined: Sat Dec 12, 2009 10:43 pm
Location: Northern California

Re: 'Damming ' with iridescent glass

Post by Charlotte Kay »

Hi Havi,

Also read Dr. Steve Immerman's excellent tutorial on dams. Scroll to the bottom for example of deep work.

http://www.clearwaterglass.com/Tutorial ... print.html

He mentions that cutting and fitting the glass with precision is the key. Use a Morton cutting system or similar. Also, squaring up the dams (ship lap) , 1/8 fiber, and then thin fire facing the irid glass.

My big block came out fine except one corner was a little askew (due to a measuring/squaring up issue as I did not have my Morton System then) but other than that it did not need cold work.

There is a new Patty Gray mold "Big Dam Mold" 8" x10" x 5/8" that might be helpful if you can find it in Israel:

http://www.sunshineglass.com/rcol/b_fus ... lds-36.htm

Hope this helps. :) I am just a beginner (3 years) but have learned so much from the generous board members!
Havi
Posts: 619
Joined: Wed Jul 02, 2003 6:01 am
Location: Israel
Contact:

Re: 'Damming ' with iridescent glass

Post by Havi »

Thanks a lot, Charlotte,

Looked at Immerman's website and saw what you meant.

Thank you


Havi
Haviva Z
- - - - with a smile :)

"Speed comes from the Devil" - (an Arabic proverb)
Image
http://www.havivaz.com