I'm stumped on this and would welcome some ideas.
I'm making a stained glass panel for a client -- a garden scene with a morning glory vine running up one side. She can't find a blue color that she likes for the morning glories. The closest we've come is the color of BE0334 or BE0114 ... but she wants more of a seedy cathedral. (Like Kokomo seedy, but we couldn't find the right blue.)
So what to do? My current thought is to take some thin BE0114 or BE0334 and fuse it with a layer of thin clear. Would the result be less "dense", and more cathedral? If I fused thin BE1114 (cathedral) with clear would it be less intense blue? Would a layer of frit work?
I don't mind doing the experiments, but I'm curious if this will be blind alley or is worth pursuing. Has anyone tried this?
Thanks! Marilyn
blending colors
Moderators: Brad Walker, Tony Smith
-
- Posts: 22
- Joined: Wed Mar 12, 2003 10:27 am
- Location: Boulder, CO
Sometimes you have to layer a couple of pieces of glass to get a good color match in restoration. It doesn't necessarily have to be fused. This eliminates the compatability issue. You just have to be sure you don't get seepage between the glasses when you cement the panel. Lots of color-making opportunities here!
Good luck,
Dani
Good luck,
Dani
-
- Posts: 56
- Joined: Mon Mar 10, 2003 6:57 pm
- Location: west central Indiana
- Contact:
-
- Posts: 2339
- Joined: Tue Mar 11, 2003 12:06 am
- Location: Chatham NH
- Contact:
Re: blending colors
MarylinMarilyn Kaminski wrote:I'm stumped on this and would welcome some ideas.
I'm making a stained glass panel for a client -- a garden scene with a morning glory vine running up one side. She can't find a blue color that she likes for the morning glories. The closest we've come is the color of BE0334 or BE0114 ... but she wants more of a seedy cathedral. (Like Kokomo seedy, but we couldn't find the right blue.)
So what to do? My current thought is to take some thin BE0114 or BE0334 and fuse it with a layer of thin clear. Would the result be less "dense", and more cathedral? If I fused thin BE1114 (cathedral) with clear would it be less intense blue? Would a layer of frit work?
I don't mind doing the experiments, but I'm curious if this will be blind alley or is worth pursuing. Has anyone tried this?
Thanks! Marilyn
You could also try painting on a transparent blue enamel.
Bert
Bert Weiss Art Glass*
http://www.customartglass.com
Furniture Lighting Sculpture Tableware
Architectural Commissions
Bert Weiss Art Glass*
http://www.customartglass.com
Furniture Lighting Sculpture Tableware
Architectural Commissions