90 COE & System 96 ??
Moderators: Brad Walker, Tony Smith
90 COE & System 96 ??
Sorry for the question, but I am very new to fusing and am trying to figure it out. So, what will happen if you mix COE 90 and 96 glass together? Someone told me that it would explode and ruin your kiln. Is this true? Any info appreciated. TIA
-
- Posts: 270
- Joined: Sun Mar 09, 2003 5:43 pm
- Location: British Columbia, Canada
- Contact:
COE stands for coefficient of expansion. 90 and 96 mean that those two types of glass expand and contract at different rates. Therefore if you mix the two when they are cooling they will contract differently and break apart. It may not "explode" or hurt your kiln but you cannot make something that will stay in one piece from two different COE glasses.
Amy
Amy
-
- Posts: 224
- Joined: Mon Mar 31, 2003 12:35 pm
- Location: Virginia
- Contact:
Explode is a term we like to use.. but crack is probally a better term.. and I doubt it will hurt the kiln unless the kiln has feelings and it will get upset that it produces cracked unusable pieces.
Look in the tutorial for a topic on compatable glass and or COE.
Look in the tutorial for a topic on compatable glass and or COE.
Kiln Repair by a Clayman kilnrepair@yahoo.com
Glassworks by a Clayman
http://www.GlassArtists.org/GlassworksByAClayman
Glassworks by a Clayman
http://www.GlassArtists.org/GlassworksByAClayman
-
- Posts: 113
- Joined: Sun Mar 09, 2003 10:10 pm
- Location: Ohio
What everyone before me has said. Now do yourself a big big favor and buy Brad's book Contempory Warm Glass. It is offered on this site and at some of the sponsors of the list. It is the best beginners book I have read. Still teething on warm glass I have read several and Brad's book is the best first book. I keep it about 4 steps from my kiln and work area at all times. There are other books that you should read after this one but they aren't as easy to understand until you have fused a little while. Nanc