hi all, I need to slump two layer of 1/2" Float glass into a sink mold (matel mold ) I have slumped sinks in the past using one layer 3/4" of Float glass @ Temperature of 1160 F.
Is 1160 F an adequate max temperature to fuse and slump two layer of
Float glass together properly into a sink ?
If not, can you recommed a temperature adequate for carrying out a
two-layer fuse and slump?
thanks?
Dartina,
A temperature for slump and fuse into sink mold
Moderators: Brad Walker, Tony Smith
-
- Posts: 2339
- Joined: Tue Mar 11, 2003 12:06 am
- Location: Chatham NH
- Contact:
Dartina
If you can get the glass to move at 1160 that is great. I usually go quite a bit hotter. It really depends on what size mold, or what size drop. Heavy glass is more cooperative than thinner glass. My work is always textured first so I don't mind dealing with the effects of hotter glass. If you want smooth 1160 is probably pretty good. 1140 is the temp I have always heard yields no marks. I must admit that I have never made that work for me. For my 16" ss bowl molds I go to 1285. For a drop mold with a larger opening, I go to 1240. For both I soak until it is done.
If you can get the glass to move at 1160 that is great. I usually go quite a bit hotter. It really depends on what size mold, or what size drop. Heavy glass is more cooperative than thinner glass. My work is always textured first so I don't mind dealing with the effects of hotter glass. If you want smooth 1160 is probably pretty good. 1140 is the temp I have always heard yields no marks. I must admit that I have never made that work for me. For my 16" ss bowl molds I go to 1285. For a drop mold with a larger opening, I go to 1240. For both I soak until it is done.
Bert
Bert Weiss Art Glass*
http://www.customartglass.com
Furniture Lighting Sculpture Tableware
Architectural Commissions
Bert Weiss Art Glass*
http://www.customartglass.com
Furniture Lighting Sculpture Tableware
Architectural Commissions
fuse and slump help
I have been fusing and slumping sinks for quite awhile now. There are numberous answers to your question but I need the following info in order to help you out.....
Your exact fusing schedule ............and your exact slumping schedule that you have used for 3/4" float. I can then relate that to the two layers. Also type of kiln.
Your exact fusing schedule ............and your exact slumping schedule that you have used for 3/4" float. I can then relate that to the two layers. Also type of kiln.
Thanks Bert,
The size of the glass is 20" round 1/2"thick, two layer of float glass
to slump and fuse into ( the same time) a metal mold for sink.
My question is ? If I go to Temp. 1285 F the Thickness of the sink wall will
be even still ? or I have to fuse two layer together first and slump.
Thanks again.
Dartina,
The size of the glass is 20" round 1/2"thick, two layer of float glass
to slump and fuse into ( the same time) a metal mold for sink.
My question is ? If I go to Temp. 1285 F the Thickness of the sink wall will
be even still ? or I have to fuse two layer together first and slump.
Thanks again.
Dartina,
-
- Posts: 2339
- Joined: Tue Mar 11, 2003 12:06 am
- Location: Chatham NH
- Contact:
I can't imagine that you can fuse and slump anything in to a bowl mold in one firing. I would always fuse between 1420 and 1435. I have written schedules for fusing before. do a search.DIHLEE wrote:Thanks Bert,
The size of the glass is 20" round 1/2"thick, two layer of float glass
to slump and fuse into ( the same time) a metal mold for sink.
My question is ? If I go to Temp. 1285 F the Thickness of the sink wall will
be even still ? or I have to fuse two layer together first and slump.
Thanks again.
Dartina,
Bert
Bert Weiss Art Glass*
http://www.customartglass.com
Furniture Lighting Sculpture Tableware
Architectural Commissions
Bert Weiss Art Glass*
http://www.customartglass.com
Furniture Lighting Sculpture Tableware
Architectural Commissions
sink molds
Where can I get a mold for a sink? Are most of them a standard size? And finally, can you use stainless bowls from Walmart? Thanks, Ginny
Re: sink molds
i found a 22" wok in a restaurant supply place for less than $30. they had bigger and smaller ones.Queenbee wrote:Where can I get a mold for a sink? Are most of them a standard size? And finally, can you use stainless bowls from Walmart? Thanks, Ginny
-
- Posts: 2339
- Joined: Tue Mar 11, 2003 12:06 am
- Location: Chatham NH
- Contact:
Re: sink molds
I haven't yet tried restaurant supply ss bowls. The 2 problems I would envision are that the walls are too steep so the glass will wrinkle as it slumps. THis could be very interesting, or not... The other is the shiny surface is probably a challenge to get kiln wash to stick to. sandblast if there is a problem. Remember to heat the bowl to 1200 then cool to 500 before you spray kiln wash on.Queenbee wrote:Where can I get a mold for a sink? Are most of them a standard size? And finally, can you use stainless bowls from Walmart? Thanks, Ginny
I wouldn't use a mild steel wok. Stainless steel is good though.
Bert
Bert Weiss Art Glass*
http://www.customartglass.com